| Property/Method |
Unit |
Condition |
Value |
| Density,
ASTM D 792 |
kg/m3
(g/cm3) |
-- |
930
(0.930) |
| Tensile
Strength, ASTM D 638b |
MPa
(psi) |
-20°C
(-4.0°F)
23°C (73°F)
49°C (120°F) |
20
(2 900)
14 (2 100)
9.0 (1 300) |
| Elongation,
ASTM D 638b |
% |
-20°C
(-4.0°F)
23°C (73°F)
49°C (120°F) |
500
600
600 |
| Vicat
Softening Temperature, ASTM D 1525 |
°C
(°F) |
-- |
73
(163) |
| Flexural
Modulus, ASTM D 790 |
MPa
(psi) |
-20°C
(-4.0°F)
23°C (73°F)
49°C (120°F) |
361
(52 400)
83 (12 000)
45 (6 500) |
| Stiffness |
MPa
(psi) |
-20°C
(-4.0°F)
23°C (73°F) |
204
(29 600)
80 (11 600) |
| Hardness,
ASTM D 2240 |
Shore
A/Shore D |
-- |
95/46 |
| Brittleness
Temperature, ASTM D 762 |
°C
(°F) |
-- |
<
-100 (< -148) |
| Compression
Set, ASTM D 395, Method B |
% |
10
days at
25°C (77°F)
22 hours at
70°C (158°F) |
45
80 |
| Tensile
Impact, ASTM D 1822 |
kJ/m2
(ft-lb/in2) |
-20°C
(-4.0°F)
23°C (73°F) |
335
(760)
400 (190) |